The low-temperature sinterability of TiO₂-CuO systems was investigated using a solid solution of SnO₂. Sample powders were prepared through conventional ball milling of mixed raw powders. With the SnO₂ content, the compositions of the samples were Ti_1-xSn_xO₂-CuO(2 wt.%) in the range of x ≤ 0.08. Compared with the samples without SnO₂ addition, the densification was enhanced when the samples were sintered at 900°C. The dominant mass transport mechanism seemed to be grain-boundary diffusion during heat treatment at 900°C, where active grain-boundary diffusion was responsible for the improved densification. The rapid grain growth featured by activated sintering was also obstructed with the addition of SnO₂. This suggested that both CuO as an activator and SnO₂ dopant synergistically reduced the sintering temperature of TiO₂.

The bone cement used for vertebroplasty must be sufficiently injectable. The introduction of granules reduces the amount of liquid required for liquefaction, implying that higher fluidity is achieved with the same amount of liquid. By employing β-tricalcium phosphate granules with an average diameter of 50 μm, changes in injectability are observed based on the paste preparation route and granular fraction. To obtain acceptable injectability, phase separation must be suppressed during injection, and sufficient capillary pressure to combine powder and liquid must work evenly throughout the paste. To achieve this, the granules should be evenly distributed. Reduced injection rates are observed for dry mixing and excessive granular content, owing to phase separation. All these correspond to conditions under which the clustered granules weakened the capillary pressure. The injected ratio of the paste formed by wet mixing displayed an inverted U-type shift with the granular fraction. The mixture of granules and powder resulted in an increase in the solid volume fraction, and a decrease in the liquid limit. This resulted in the enhancement of the liquidity, owing to the added liquid. It is inferred that the addition of granules improves the injectability, provided that the capillary pressure in the paste is maintained.

Ti_0.5Al_0.5N/CrN nano-multilayers, which are known to exhibit excellent wear resistances, were prepared using the unbalanced magnetron sputter for various periods of 2–7 nm. Ti_0.5Al_0.5N and CrN comprised a cubic structure in a single layer with different lattice parameters; however, Ti_0.5Al_0.5N/CrN exhibited a cubic structure with the same lattice parameters that formed the superlattice in the nano-multilayers. The Ti_0.5Al_0.5/CrN multilayer with a period of 5.0 nm exceeded the hardness of the Ti_0.5Al_0.5N/CrN single layer, attaining a value of 36 GPa. According to the low-angle X-ray diffraction, the Ti_0.5Al_0.5N/CrN multilayer maintained its as-coated structure up to 700°C and exhibited a hardness of 32 GPa. The thickness of the oxidation layer of the Ti_0.5Al_0.5N/CrN multilayered coating was less than 25% of that of the single layers. Thus, the Ti_0.5Al_0.5N/CrN multilayered coating was superior in terms of hardness and oxidation resistance as compared to its constituent single layers.

Nanoparticles of PbTe are prepared via chemical reaction of the equimolar aqueous solutions of Pb(CH₃COO)₂ and Te at 120°C. The size of the obtained particles is 100 nm after calcination in a hydrogen atmosphere. Dense specimens for the thermoelectric characterization are produced by spark plasma sintering of prepared powders at 400°C to 500°C under 80 MPa for 5 min. The relative densities of the prepared specimens reach approximately 97% and are identified as cubic based on X-ray diffraction analyses. The thermoelectric properties are evaluated between 100°C and 300°C via electrical conductivity, Seebeck coefficient, and thermal conductivity. Compared with PbTe ingot, the reduction of the thermal conductivities by more than 30% is verified via phonon scattering at the grain boundaries, which thus contributes to the increase in the figure of merit.

Citations

Citations to this article as recorded by  

• Improved Thermoelectric Performance of Cu3Sb1−x−ySnxInySe4 Permingeatites Double-Doped with Sn and In
  Ho-Jeong Kim, Il-Ho Kim
  Korean Journal of Metals and Materials.2023; 61(6): 422.     CrossRef
• Enhancing Electrical Properties of N-type Bismuth Telluride Alloys through Graphene Oxide Incorporation in Extrusion 3D Printing
  Jinhee Bae, Seungki Jo, Kyung Tae Kim
  journal of Korean Powder Metallurgy Institute.2023; 30(4): 318.     CrossRef